PC 合金   PC 合金   PC 合金

  Makroblend  UT3905 Bayer AG PC+PBT Makroblend  UT3905 Bayer AG PC+PBT Bayer AG Makroblend  UT3905 PC+PBT

  Makroblend  UT3907 Bayer AG PC+PBT Makroblend  UT3907 Bayer AG PC+PBT Bayer AG Makroblend  UT3907 PC+PBT

  Makroblend  UT4045 G Bayer AG PC+PET Makroblend  UT4045 G Bayer AG PC+PET Bayer AG Makroblend  UT4045 G PC+PET

  Makroblend  UT6005 Bayer AG PC+PBT Makroblend  UT6005 Bayer AG PC+PBT Bayer AG Makroblend  UT6005 PC+PBT

  Makroblend  UT6007 Bayer AG PC+PBT Makroblend  UT6007 Bayer AG PC+PBT Bayer AG Makroblend  UT6007 PC+PBT

  Makrofol  BL 6-2 820802 Bayer LLC PC Makrofol  BL 6-2 820802 Bayer LLC PC Bayer LLC Makrofol  BL 6-2 820802 PC

  Makrofol  BL 6-2 820803 Bayer LLC PC Makrofol  BL 6-2 820803 Bayer LLC PC Bayer LLC Makrofol  BL 6-2 820803 PC

  Makrofol  BL 6-2 820812 Bayer LLC PC Makrofol  BL 6-2 820812 Bayer LLC PC Bayer LLC Makrofol  BL 6-2 820812 PC

  Makrofol  BL 6-2 95/802 Bayer LLC PC Makrofol  BL 6-2 95/802 Bayer LLC PC Bayer LLC Makrofol  BL 6-2 95/802 PC

  Makrofol  BL 6-2 95/803 Bayer LLC PC Makrofol  BL 6-2 95/803 Bayer LLC PC Bayer LLC Makrofol  BL 6-2 95/803 PC

  Makrofol  BL 6-2 95/812 Bayer LLC PC Makrofol  BL 6-2 95/812 Bayer LLC PC Bayer LLC Makrofol  BL 6-2 95/812 PC

  Makrofol  DE 1-1 Baye

1. PC(聚碳酸酯#防弹胶)/300-15/陶氏杜邦

   用途： 其它

   特性备注：优异的抗冲击强度、透明度和耐热性

   重要参数： 熔体流动速率:15 g/10min 密度:1.2 g/cm3 断裂伸长率:150 % 弯曲强度:97 MPa 弯曲模量:2400 MPa 维卡软化点:148 ℃ 热变形温度:124 ℃ 透光率:89 %

   生产厂商：陶氏杜邦公司 

2. PC(聚碳酸酯#防弹胶)/300 TFE 15 SI/美国RTP

   用途： 其它

   重要参数： 密度:1.28 g/cm3 吸水率:0.1 % 成型收缩率:0.6 % 断裂伸长率:8.5 % 弯曲强度:79.3 MPa 弯曲模量:2070 MPa 热变形温度:135 ℃

   生产厂商：美国RTP公司 

3. PC(聚碳酸酯#防弹胶)/ESD 300 EM TFE 15/美国RTP

   用途： 其它

   重要参数： 密度:1.41 g/cm3 成型收缩率:0.1 % 断裂伸长率:1 % 弯曲强度:131 MPa 弯曲模量:14500 MPa 热变形温度:143 ℃

   生产厂商：美国RTP公司 

4. PC(聚碳酸酯#防弹胶)/300 TFE 15 SI Z/美国RTP

   用途： 其它

   重要参数： 密度:1.28 g/cm3 成型收缩率:0.5 % 断裂伸长率:10 % 弯曲强度:75.8 MPa 弯曲模量:2070 MPa 热变形温度:129 ℃

   生产厂商：美国RTP公司